THERMALLY INDUCED FULLERENE DOMAIN COARSENING PROCESS IN ORGANIC SOLAR CELLS

thermally

ABSTRACT

The recent advancements in power conversion efficiency for organic solar cells is still complained by their reliability and stability remaining the main bottlenecks for organic photovoltaics large scale production and commercialization. In this paper, we aim to provide further insights understanding in degradation processes affecting stability in small molecule flat heterojunction (Glass/ITO/MoO₃/ZnPc/C₆₀/BCP/Ag) solar cells through a systematic aging study coupled with optoelectrical characterizations. In particular, the burn-in phenomenon affecting short-circuit current in thermal-stressed samples has been clearly correlated with the C₆₀ domain coarsening process and eventually to the decreased exciton lifetime.

Antonio Agresti, Sara Pescetelli, Yan Busby, Tom Aernouts

DOI: 10.1109/TED.2018.2880760

IEEE Transactions on Electron Devices PP(99):1-11 · November 2018

https://www.researchgate.net/publication/329199419_Thermally_Induced_Fullerene_Domain_Coarsening_Process_in_Organic_Solar_Cells

 

 

logo University of Rome Tor Vergata
Università degli Studi di Roma
"Tor Vergata"


logo Regione Lazio

Questo sito web utilizza i cookie per capire come viene utilizzato il sito e per permettere l'accesso all'area riservata. I cookie non permettono di identificare l'utente. I cookie sono salvati sul tuo browser e sono utlizzati per personalizzare la tua esperienza sul nostro sito web. Continuando la navigazione sul nostro sito senza modificare le impostazioni, accetti il nostro utilizzo dei cookie. Comunque potrai modificare le tue impostazioni dei cookie in qualsiasi momento.