Breaking news: CHOSE push the record of Perovskite module efficiency up to 13%

Researchers of CHOSE fabricated a Perovskite module on 10cm2 active area with a record efficiency of 13%. The results of the work have been published on Progress in Photovoltaics.

ABSTRACT
We fabricated monolithic solid state modules based on organometal CH3NH3PbI3 and CH3NH3PbI3-xClx perovskites using poly-(3-hexylthiophene) and Spiro-OMeTAD as hole transport materials (HTMs). In particular, we developed innovative and scalable patterning procedures to minimize the series resistance at the integrated series-interconnections. By using these optimization steps, we reached a maximum conversion efficiency of 8.2% under AM1.5G at 1 Sun illumination conditions using the CH3NH3PbI3-xClx perovskite and the poly-(3-hexylthiophene) as HTM. Finally, we investigated the double-step deposition of CH3NH3PbI3 using the Spiro-OMeTAD, reaching a maximum conversion efficiency on active area (10.08 cm2) equal to 13.0% (9.1% on aperture area) under AM1.5G at 1 Sun illumination conditions. This remarkable result represents the highest PCE value reached for the perovskite solar modules.

 
Questo sito web utilizza i cookie per capire come viene utilizzato il sito e per permettere l'accesso all'area riservata. I cookie non permettono di identificare l'utente. I cookie sono salvati sul tuo browser e sono utlizzati per personalizzare la tua esperienza sul nostro sito web. Continuando la navigazione sul nostro sito senza modificare le impostazioni, accetti il nostro utilizzo dei cookie. Comunque potrai modificare le tue impostazioni dei cookie in qualsiasi momento.